Abstract
A discussion about the isothermal tuning of exchange bias (HE) and coercivity (HC) of antiferromagnetic (AFM)/ ferromagnetic bilayers was presented. It was found that the HE and HC were controlled at room temperature, after a sample growth, by applying pulsed fields. The effects observed in textured Fe50Mn50 based bilayers showed a decrease in HE while HC can either increase or decrease depending on the direction of the pulsed field.
Original language | English |
---|---|
Pages (from-to) | 3044-3046 |
Journal | Applied physics letters |
Volume | 82 |
DOIs | |
Publication status | Published - 5 May 2003 |