Biomimetic Replication of Microscopic Metal-Organic Framework Patterns Using Printed Protein Patterns

Kang Liang, Carlos Carbonell, Mark J. Styles, Raffaele Ricco, Jiwei Cui, Joseph J. Richardson, Daniel Maspoch, Frank Caruso, Paolo Falcaro

    Producció científica: Contribució a revistaArticleRecercaAvaluat per experts

    106 Cites (Scopus)

    Resum

    An experiment was conducted to demonstrate that zeolitic imidazolate framework-8 (ZIF-8) and lanthanide ions (Ln2) (bdc)3 crystalline thin films and patterns can be formed as a result of biomimetic replication directly from protein patterns on various surfaces. This rapid process was performed in aqueous conditions at room temperature with a resolution in the micrometer range. Aqueous bovine serum albumin (BSA) solutions were prepared. A clean and dry ink pad was soaked in the BSA solution and removed. For the formation of ZIF-8 thin films and patterns, separate stock solutions of zinc acetate dehydrate and 2-methylimidazole were prepared in deionized water. These two solutions were mixed and immediately transferred onto the BSA patterns. After 12 h, the formed ZIF-8 patterns were washed three times in ethanol and dried under a stream of N2. For the formation of Ln2) (bdc)3 thin films and patterns, separate stock solutions of LnCl3 hydrate and terephthalic acid disodium salt were prepared in deionized water. These two solutions were mixed and immediately transferred onto the BSA patterns. After 30 s, the formed luminescent metal?organic frameworks (MOF) patterns were washed three times in deionized water and dried under a stream of N2.
    Idioma originalAnglès
    Pàgines (de-a)7293-7298
    RevistaAdvanced Materials
    Volum27
    Número45
    DOIs
    Estat de la publicacióPublicada - 1 de gen. 2015

    Fingerprint

    Navegar pels temes de recerca de 'Biomimetic Replication of Microscopic Metal-Organic Framework Patterns Using Printed Protein Patterns'. Junts formen un fingerprint únic.

    Com citar-ho